Influence of specific pressure of pressing and firing temperature on frost resistance of the modified laboratory samples from atyukhtinsky clay raw materials
Abstract
Influence of specific pressure of pressing and firing temperature on frost resistance of the modified laboratory samples from atyukhtinsky clay raw materials
Incoming article date: 04.12.2013Results of researches on joint influence of specific pressure of pressing and firing temperature on physico-mechanical properties of laboratory samples on the basis of atyukhtinsky clay raw materials is shown. For the purpose of increase of frost resistance of the burned samples into structure of masses entered a carbonat containing modifying additive in an amount of 5%. For a quantitative assessment of influence of the specified factors on the main indicators of the burned samples researches with application of mathematical planning of experiment and computer processing of results were conducted. Specific pressure of pressing varied within 20±5 MPa, firing temperature – 1000±50 0C. By results of experiment the regression equations are received. It is defined that at increase of value of both varied factors, frost resistance and durability of samples increase, and water absorption – decreases. It is shown that, operating even with two technology factors – the specific pressure of pressing and firing temperature – it is possible to change significantly properties of finished products, and, using the received equations, it is possible to predict future properties of products at a stage of their production.
Keywords: frost resistance, burned sample, modifying additive, specific pressing pressure, firing temperature, mathematical experiment planning